硫酸盐系聚阴离子型正极材料凭借其在电负性、工作电压和成本方面的优势，被认为是未来最具潜力的钠离子电池正极材料之一。本文首先探讨了钠离子电池正极材料硫酸铁钠的全球专利申请趋势，然后对钠离子电池正极材料硫酸铁钠申请量排名前十的申请人进行梳理分析，并重点从六大方面归纳分析全球范围内的专利技术进展。最后从完善专利布局和加强海外专利的保护等方面，给出总结与建议。
Abstract：Sulfate-based polyanion-type cathode materials are considered as one of the most promising cathode materials for sodium-ion batteries due to their electronegativity, working voltage, and cost in the future.This article first discusses the global patent application tendency of sodium iron sulfate cathode materials for sodium-ion batteries.Then, it analyzes the top ten applicants of application quantity concerning sodium iron sulfate cathode materials for sodium-ion batteries, and focuses on summarizing and analyzing the global patent technology progress from six aspects.And conclusions and suggestions are given in order to improve patents layout and strengthen the protection of overseas patents.
[1] BARPANDA P,OYAMA G,NISHIMURA S I,et al.A 3.8 V earth-abundant sodium battery electrode[J].Nature Communications,2014,5:4358.
[2] 张敏.钠离子电池正极材料硫酸亚铁钠的制备及电化学性质研究[D].长春：吉林大学，2018.
[3] 颜晨星.硫酸铁钠类材料的制备与电化学性能研究[D].徐州：中国矿业大学，2017.
[4] BARPANDA P,OYAMA G,LING C D,et al.Kr?hnkite-type Na2Fe(SO4)2·2H2O as a novel 3.25 V insertion compound for Na-ion batteries[J].Chemistry of Materials,2014,26(3):1297-1299.
[5] MENG Y,ZHANG S,DENG C.Superior sodium-lithium intercalation and depressed moisture sensitivity of a hierarchical sandwich-type nanostructure for a graphene-sulfate composite:A case study on Na2Fe(SO4)2·2H2O[J].Journal of Materials Chemistry A,2015,3(8):4484-4492.
[6] OYAMA G,NISHIMURA S I,SUZUKI Y,et al.Off-stoichiometry in alluaudite-type sodium iron sulfate Na2+2xFe2-x(SO4)3 as an advanced sodium battery cathode material[J].ChemElectroChem,2015,2(7):1019-1023.
[7] 方永进，陈重学，艾新平，等.钠离子电池正极材料研究进展[J].物理化学学报，2017,33(1):211-241.
[8] 穗积正人，后田伸，二井谷启太，等.钠离子传导体和钠离子固体电池：CN112768751A[P].2021-05-07.
[9] 中央硝子株式会社.非水电解液、非水电解液电池及化合物：WO,JP2022/003342[P].2022-08-11.
[10] 宁德时代新能源科技股份有限公司.钠离子电池和包含钠离子电池的装置：WO,CN2020/072453[P].2020-08-06.
[11] 陈卫华，张继雨，颜永亮，等.微米级多孔硫酸亚铁钠/碳复合正极材料及其制备的钠离子电池或钠电池：CN114050246B[P].2023-02-07.
[12] 赵建庆，王齐，陈宇，等.一种碳包裹的硫酸铁钠正极材料及其制备方法：CN115020681A[P].2022-09-06.
[13] 苏州高博储能科技有限公司.铁基钠离子电池正极材料及其制备方法：中国，CN201911252756.4[P].2020-11-24.
[14] 江苏众钠能源科技有限公司.一种正极材料、正极极片及钠离子电池：中国，CN202310624983.5[P].2023-12-29.
[15] 时爽二，庞晨阳，戚昌伟，等.一种钠离子电池正极材料及其制备方法、钠离子电池：CN112563484B[P].2022-08-19.
[16] FARADION LTD.SULFATE ELECTRODES:WO,GB 2013/050198[P].2013-08-08.
[17] 赵建庆，李哲，贾琪婷，等.一种混合活性材料及锂钠混用离子电池：CN115954466B[P].2023-06-06.
[18] 赵阿龙，曹余良，陈晓洋，等.具有界面修饰层的聚阴离子型钠离子电池正极材料制备方法：CN116885149A[P].2023-10-13.
[19] 深圳珈钠能源科技有限公司.空气稳定性高的硫酸盐类钠离子电池正极材料及其制备方法：中国，CN202311576040.6[P].2024-02-23.
[20] 江苏中兴派能电池有限公司.一种钠离子电池正极极片、其制备方法及钠离子电池：中国，CN202311551118.9[P].2024-01-30.
基本信息:
DOI：10.19996/j.cnki.ChinBatlnd.2024.04.009
中图分类号:TM912;G255.53
引用信息:
[1]朱碧玉,王韶华,胡彦玲.钠离子电池正极材料硫酸铁钠专利技术分析[J].电池工业,2024,28(04):206-211+220.DOI:10.19996/j.cnki.ChinBatlnd.2024.04.009.
2024-03-11
2024
2024-05-15
2024
1
2024-06-20
2024-06-20
2024-06-20